Comparative evaluation of physical anatomical parameters that influence the side glue of wood panels of Pinus Elliottii and Pinus Taeda

Authors

DOI:

https://doi.org/10.5965/2316419010172021031

Keywords:

Pine Furniture, Side Gluing, Isocyanate Polymer Emulsion, Mechanical Properties of Glued Elements

Abstract

The main interests aroused in this work were the application of more effective technologies to improve the wood-adhesive interaction in glued panels, guaranteeing dimensional stability, thus ensuring the quality of products used in Pinusfurniture generated from EGP (Edge Glued Panel -panel with side glue). Aiming to evaluate the strength and wood-adhesive interaction of the glue line in EGP wood panels of Pinuselliottiiand Pinustaedalaterally glued with an adhesive based on polymeric isocyanate emulsion (EPI). In the production of joints of wooden parts, different machining processes were used (moulding machine, sandpaper and saw), parts with moisture contents (8 and 15%) and dimensions (slats with thickness 45 and 60 mm). The physical properties of the wood species of the bonded elements were evaluated, evaluating lateral bonding and end bonding through end joints (finger joint). The anatomical analyzes showed that the two Pinusspecies did not present significant differences between them (p˂0.05), and that factors such as wood density and moisture content of the studied slats did not influence the mechanical properties of the panels. The shear strength of P. elliottiiand P. taedaspecies were 137.03 kgf/cm2and 149.36 kgf/cm2, respectively. The highest tensile strength of finger jointseams, (262.64 kgf/cm2) was obtained by bonding the species and P. taeda. Analyzing the requirements of the standards, all species met the minimum values required for both wood failure and mechanical strength.

Downloads

Author Biographies

João Carlos Ferreira de Melo Júnior, University of Joinville Region, UNIVILLE, Brazil.

PhD in Ecology and Conservation from the Paraná Federal University, UFPR, Brazil.

Has a Master’s degree in Botany from the Paraná Federal University, UFPR, Brazil.

Specialist in Space Society and Environment from the Brazilian Institute of Graduate Studies and Extension, IBPEX, Brazil.

Graduated in Biological Sciences at the University of the Region of Joinville, UNIVILLE, Brazil.

Professor at the University of the Region of Joinville, UNIVILLE, Brazil.

Adriano Bolgenhagen, University of Joinville Region, UNIVILLE, Brazil.

Specialist in Production Engineering from the International University Center, UNINTER, Brazil.

Graduated in Production Engineering (Mechanical Qualification) at the Santa Catarina State University, UDESC, Brazil.

Graduated in Mechanical Technology at the Santa Catarina State University, UDESC, Brazil.

Noeli Sellin, University of Joinville Region, UNIVILLE, Brazil.

PhD in Chemical Engineering from the University of Campinas, UNICAMP, Brazil.

Has a Master’s degree in Chemical Engineering from the University of Campinas, UNICAMP, Brazil.

Graduated in Chemical Engineering at the Maringá State University, UEM, Brazil.

Professor at the University of the Region of Joinville, UNIVILLE, Brazil.

References

ABIMCI - ASSOCIAÇÃO BRASILEIRA DA INDÚSTRIA DE MADEIRA PROCESSADA MECANICAMENTE – Estudo setorial 2019 da indústria de madeira processada mecanicamente. Curitiba, 2019.

ABIPA – ASSOCIAÇÃO BRASILEIRA DA INDÚSTRIA DE PAINÉIS DE MADEIRA. Estudo setorial Disponível em: http://www.abipa.org.br >. Acesso em: 04/06/2020.

ABNT - ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICA. Especificações geométricas do produto (GPS) - Rugosidade: Método do perfil - Termos, definições e parâmetros da rugosidade. NBR ISO 4287 – 2002.

ABNT - ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. Madeira – Amostragem e preparação para análise. NBR 14660. 2004. 18 p

ABNT - ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. Madeira – Determinação da densidade básica. NBR 11941. 2003. 24 p.

ABNT - ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. Madeira – Determinação do teor de umidade de cavacos. NBR 14929. 2017. 17 p.

ABNT - ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS. Projetos de estruturas de madeira. NBR 7190. Rio de Janeiro, 1997. 107 p.

ALMEIDA, V. C. Avaliação do potencial de uso de resíduos de madeira tropical para produção de painéis colados lateralmente – EGP. Tese (Doutorado em Engenharia Florestal), Universidade Federal do Paraná, Curitiba, 2013.

ASTM - AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM D5572: Standard Specification for Adhesives Used for Finger joints in Nonstructural Lumber Products. 2006.

ASTM - AMERICAN SOCIETY FOR TESTING AND MATERIALS. ASTM D5751 – 99: (rev 2005) Standard specification for adhesives used for laminate joints in nonstructural lumber products. Pennsylvania, 1995. 11 p.

BIANCHE, J. J. Interface madeira-adesivo e resistência de juntas coladas com diferentes adesivos e gramatura. Federal de Viçosa. Viçosa, MG, 2014. Tese de doutorado.

BILA, N. F. Avaliação da qualidade de juntas coladas de seis espécies de madeiras tropicais da Amazônia. Dissertação (Mestrado em Ciências Florestais) - Setor de Ciências Agrárias, Universidade Federal do Paraná, Curitiba, Paraná. 2014.

CARVALHO, M. Z. Abordagem multivariada do comportamento das propriedades físico-químicas e caracterização de adesivos naturais à base de taninos. Lavras: UFLA, 2016. 135 p. Tese de doutorado.

COPANT - Comisión Panamericana de Normas Técnicas – Norma 461- Maderas: método de determinación del peso especifico aparente, 1972 (COPANT 30: 1-004, 1971)

COPANT - Comisión Panamericana de Normas Técnicas – Norma 462- Maderas: método de determinación de la contracción, 1972 (COPANT 30: 1-004, 1971)

FOGAÇA, A. P. Determinação da qualidade de colagem e desempenho mecânico de painéis EGP comerciais. Trabalho de conclusão de curso (bacharelado - Engenharia Industrial Madeireira) - Universidade Estadual Paulista Júlio de Mesquita Filho, Campus de Itapeva, 2014.

FONTE, A. P. N. Utilização da madeira de cryptomeria japonica para a produção de painéis colados lateralmente e aplicação de acabamento superficial. Dissertação apresentada ao Programa de Pós-Graduação em Engenharia Florestal, Universidade Federal do Paraná, 2016.

IAWA COMMITTEE. List of microscopic features for hardwood identification. IAWA Bulletin, v. 10, p. 220-332, 1989.

IBA – INDUSTRIA BRASILEIRA DE ÁRVORES. Indicadores de desempenho de árvores plantadas – ano base 2016. 80 p. – Brasília, DF, 2016

IWAKIRI, S.; BILA, F. N.; TRINOSKI, R.; PRATA, G. J. Avaliação da qualidade de juntas coladas de seis espécies de madeiras tropicais da Amazônia. FLORESTA, [S.l.], v. 46, n. 4, p. 455-464, jan. 2017. ISSN 1982-4688.

KLOCK, U.; Qualidade da madeira juvenil de Pinus maximinoi H. E. Moore. 2000. 291f. Tese (Doutorado em Engenharia Florestal) - Universidade Federal do Paraná, Curitiba, 2000b.

LOPES, M. C.; MUNIZ, G. I. B.; MATOS, J. L. M.; TANOBE, V. O. A.; CHINASSO, C. A. F.; ROSSO, S. Resistência da linha de cola de painéis de Pinus taeda colados lateralmente com diferentes adesivos. CERNE [online]. 2013, vol.19, n.4, pp.613-619. ISSN 0104-7760.

MELO JR.; J. C. F. Anatomia de madeiras históricas: um olhar biológico sobre o patrimônio cultural. Joinville: Editora UNIVILLE, 2012.

MOTTA, J. P.; OLIVEIRA, J. T. S.; PAES, J. B.; ALVES, R. C.; VIDAURRE, G. B. Avaliação da resistência ao cisalhamento de juntas coladas com madeira de teca (Tectona grandis) evaluation of the shear strength of bonded joints of teak wood (Tectona grandis). Scientia Forestalis, Piracicaba, v. 42, n. 104, p. 615-621, 2014.

PINHEIRO, C. Efeitos do teor de umidade da madeira no fresamento de Pinus elliottii . Dissertação (mestrado) – Universidade Estadual Paulista, Faculdade de Engenharia de Guaratinguetá, 2014.

PRADO, Lucas Andre. Viabilidade do uso das colas EPI e PVAC em produtos não estruturais de madeira maciça de eucalipto. 2021. 66 f. Trabalho de Conclusão de Curso (Graduação) – Universidade Tecnológica Federal do Paraná, Guarapuava, 2021.

PRATA, J. G. Estudo da viabilidade tecnológica do uso de espécies de Pinus Tropicais para produção de painéis colados lateralmente (edge glued panels – EGP).Tese (Doutorado em Engenharia Florestal) - Ciências Agrárias, Universidade Federal do Paraná-UFPR, Curitiba, 2010.

PRATT, G. H. Timber driyng manual. London: Building Research Estabilishment, 1974, 152p.fl

RANJAN, M.; KHALI, D.P.; ISMITA, N.; KISHANKUMAR V.S.; Gupta, S. Effect of adding Urea Formaldehyde in Polyvinyl acetate on the bending properties of Finger jointed Wood sections. International Archive of Applied Sciences and Technology. 2019

TAPPI – Technical Association Of The Pulp And Paper Industry. TAPPI 252. pH and electrical conductivity of hot water extracts of pulp, paper, and paperboard. Atlanta. 2012.

TRIANOSKI, R. Avaliação da qualidade da madeira de espécies de Pinus tropicais por meio de métodos convencionais e não destrutivos. 2012. Tese. (Doutorado em Engenharia Florestal) - Universidade Federal do Paraná, Curitiba, 2012.

TRIANOSKI, Rosilani; IWAKIRI, Setsuo y BONDUELLE, Ghislaine Miranda. Qualidade das juntas coladas de madeira de cinco espécies de Eucalyptus com adesivos acetato de polivinila e resorcina-formaldeído. Madera bosques [online]. 2020, vol.26, n.3

Downloads

Published

2021-12-22 — Updated on 2021-12-22

Versions

How to Cite

Melo Júnior, J. C. F. de, Bolgenhagen, A., & Sellin, N. (2021). Comparative evaluation of physical anatomical parameters that influence the side glue of wood panels of Pinus Elliottii and Pinus Taeda. Revista Brasileira De Contabilidade E Gestão, 10(19), 031–048. https://doi.org/10.5965/2316419010172021031 (Original work published June 7, 2022)

Issue

Vol. 10 No. 19 (2021)

Section

INOVA

License

Copyright (c) 2021 João Carlos Ferreira de Melo Júnior, Noeli Sellin, Adriano Bolgenhagen

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Brazilian Journal of Accounting and Management offers free and immediate access to its content, following the principle that providing scientifical knowledge in a free manner promotes a better world democratization of knowledge. Authors maintain copyright of articles and grant to the journal the rights of the first publication, according to the Creative Commons Attribution licensing criteria, which allows the work to be shared with initial publication and authorship recognition. These licenses allow others to distribute, remix, adapt, or create derived work, even if it is for commercial purposes, provided that the credit is given to the original creation.